CHROMIUM CARBIDE OVERLAY WEAR PLATE
Moderate Abrasion Resistant Wear Plate
Chromium Carbide Overlay (CCO) Wear Plate is an extra hard clad plate with additives that gives even higher abrasion resistance in high stress applications with moderate to low impact conditions.
Features & Benefits
Cost effective solution when compared to traditional abrasion-resistant steels
Recommended for resistance to wear by abrasion, fretting, cavitation, and
particle erosion in high temperature applications (up to 1100°F).
Ideal for mild to moderate impact abrasion resistance.
Low maintenance cost and easy installation.
The overlay surface of CCO plate will consist of a series of beads with numerous
hairline cracks in them. These properly spaced crosscheck cracks are a natural
phenomenon and are beneficial to the material. The cracks propagate through the
overlay and end at the fusion line.
Cutting – Plasma burning, air arc, abrasive saw or water jet.
Welding – Our CCO overlay plate can be joined by welding the substrate to substrate using 309 weld wire/rod.
Bending – Using a press brake, forming should be perpendicular to the weld pass direction.
Plate rolling should be performed in the directions of the overlay beads.
Technical Specifications & Chemical CompositionChromium Carbid_Chemical Composition_ web
Hardness ranges from 58-62 HRC based on weld thickness
Superior wear resistance
Optimum solution for most industrial applications
White Iron Laminated Wear Plates, Bimetallic chrome white iron brazed wear plates, Laminated Wear Plate Wear Liners Bimetallic Chromium Carbide Wear Plates, laminated 700 HB / 63 HRc Wear Plates, Wear-resistant plates parts, Domite 700bhn High Chrome Cast Iron Wear Plate China supplier Laminated Wear Plates – It is a combination of high chromium white […]
Overlay Wear Plates, Wear Resistant Hardfacing Steel Plate, Chromium Overlay Wear Plate for Impact Walls, Overlay Chromium Carbide Bimetallic Wear Plate, Chromium Carbide Overlay Plate Liner, 3+3, 4+6, 10+8, 12+17 Wear Plate, 550HB-650HB Wear resistant plate China Supplier Overlay Wear Plates – OVERLAY-PLATE is welded by Chromium carbide overlay on a mild steel backing plate. […]
Mining Bimetallic Wear Bar, White Iron laminated blocks wear bars for wear ore mining protection, Weldable casting wear bars, Wear bars 63HRC white iron for ore mining machine parts, The best anti-wear material wear bars and blocks China supplier Mining Bimetallic Wear Bar – Wear bars and blocks are available in thicknesses ranging from 25mm […]
White Iron Wear Bar, Bimetallic Wear Bar, White Iron laminated blocks wear bars for wear mining protection, Weldable casting wear bars, high chromium 700HB 63HRC white iron wear bar for mining machine parts, Abrasion-proof wear bars blocks China supplier White Iron Wear Bar – Wear bar is a combination of high chromium (700 brunell) white […]